| Frequently asked property | ||
|---|---|---|
| Frequently asked property Tested acc. to ISO 1183 | g/cm³ | 1.39 |
| Temperature for usage in air | °C | 160 |
| Temperature for usage in air Tested acc. to ISO 60093 | Ohm*m [≥] | 10^13 |
| Tensile modulus of elasticity Tested acc. to ISO 527-2 | MPa | 3600 |
| Mechanical properties | ||
|---|---|---|
|
Tensile stress at yield
[v = 50 mm/min] Tested to ISO 527-2 |
MPa | 90 |
|
Tensile stress at break
[v = 50 mm/min] Tested to ISO 527-2 |
MPa | 0 |
|
Nominal elongation at break
[v = 50 mm/min] Tested to ISO 527-2 |
MPa | 15 |
|
Ball indentation hardness
[value at 30 sec.] Tested to ISO 2039-1 |
MPa | 170 |
|
Rockwell hardness
[value at 30 sec.] Tested to ISO 2039-1 |
M 95 | |
|
Charpy impact strength
[+ 23 °C] Tested to ISO 179/1eU |
kJ/m2 | 50 |
|
Charpy impact strength - notched
[+ 23 °C] Tested to ISO 179/1eA |
kJ/m2 | 3 |
| Thermal properties | ||
|---|---|---|
| Temperature for usage in air | °C | 115 |
| Minimum service temperature in air | °C | -20 |
| Heat distortion temperature (HDT A process) | °C | 75 |
|
Coefficient of linear expansion
(longitudinal, 23-60 °C) Tested to ISO 11359 |
10^(-4/K) | 0.6 |
|
Thermal conductivity
(+ 23 °C) Tested to DIN 52612 |
W/(K*m) | 0.27 |
|
Flammability according UL standard
(Thickness 3 and 6 mm) Tested to UL 94 |
Klasse | HB |
|
Vicat softening temperature
(VST/B/50) Tested to ISO 306 |
°C | 0 |
|
Melting point
DSC, 10 K/min). Tested to ISO 3146 |
°C | 255 |
| Physical properties | ||
|---|---|---|
|
Moisture pick-up till saturation
(in normal climate 23 °C / 50% r.h.) Tested to ISO 62 |
% | 0.3 |
|
Water absorption till saturation
(in water at 23 °C) Tested to ISO 62 |
% | 0.5 |
| Food compliance Tested to EU-VO 10/2011 | yes | |
| Food compliance Tested according to FDA | yes |
| Electric properties | ||
|---|---|---|
|
Specific surface resistance
[>] Tested to IEC 60093 |
Ohm | 10^14 |
|
Dielectric constant
At 1 MHz Tested to IEC 602250 |
10^6 Hz | 3.2 |
|
Dielectric constant
At 100 Hz Tested to IE C 602250 |
10^2 Hz | 3.4 |
|
Dissipation factor
At 1 MHz Tested to IEC 602250 |
10^6 Hz | 0.014 |
|
Dissipation factor
At 100 Hz Tested to IE C 602250 |
10^2 Hz | 0.001 |
|
Dielectric strength K20/K20
(in transformer oil) Tested to IEC 60243-1 |
kV/mm | 22 |
| Comparative tracking index (CTI) Tested to IEC 60112 | 600 |