Frequently asked property | ||
---|---|---|
Frequently asked property Tested acc. to ISO 1183 | g/cm³ | 1.42 |
Temperature for usage in air | °C | 150 |
Temperature for usage in air Tested acc. to ISO 60093 | Ohm*m [≥] | 10^14 |
Tensile modulus of elasticity Tested acc. to ISO 527-2 | MPa | 3600 |
Mechanical properties | ||
---|---|---|
Tensile stress at yield
[v = 50 mm/min] Tested to ISO 527-2 |
MPa | 78 |
Tensile stress at break
[v = 50 mm/min] Tested to ISO 527-2 |
MPa | 0 |
Nominal elongation at break
[v = 50 mm/min] Tested to ISO 527-2 |
MPa | 35 |
Ball indentation hardness
[value at 30 sec.] Tested to ISO 2039-1 |
MPa | 160 |
Rockwell hardness
[value at 30 sec.] Tested to ISO 2039-1 |
M 88 | |
Charpy impact strength
[+ 23 °C] Tested to ISO 179/1eU |
kJ/m2 | 220 |
Charpy impact strength - notched
[+ 23 °C] Tested to ISO 179/1eA |
kJ/m2 | 10 |
Thermal properties | ||
---|---|---|
Temperature for usage in air | °C | 105 |
Minimum service temperature in air | °C | -50 |
Heat distortion temperature (HDT A process) | °C | 115 |
Coefficient of linear expansion
(longitudinal, 23-60 °C) Tested to ISO 11359 |
10^(-4/K) | 1 |
Thermal conductivity
(+ 23 °C) Tested to DIN 52612 |
W/(K*m) | 0.31 |
Flammability according UL standard
(Thickness 3 and 6 mm) Tested to UL 94 |
Klasse | HB |
Vicat softening temperature
(VST/B/50) Tested to ISO 306 |
°C | 0 |
Melting point
DSC, 10 K/min). Tested to ISO 3146 |
°C | 175 |
Physical properties | ||
---|---|---|
Moisture pick-up till saturation
(in normal climate 23 °C / 50% r.h.) Tested to ISO 62 |
% | 0.2 |
Water absorption till saturation
(in water at 23 °C) Tested to ISO 62 |
% | 0.85 |
Food compliance Tested to EU-VO 10/2011 | yes | |
Food compliance Tested according to FDA | no |
Electric properties | ||
---|---|---|
Specific surface resistance
[>] Tested to IEC 60093 |
Ohm | 10^13 |
Dielectric constant
At 1 MHz Tested to IEC 602250 |
10^6 Hz | 3.8 |
Dielectric constant
At 100 Hz Tested to IE C 602250 |
10^2 Hz | 3.8 |
Dissipation factor
At 1 MHz Tested to IEC 602250 |
10^6 Hz | 0.008 |
Dissipation factor
At 100 Hz Tested to IE C 602250 |
10^2 Hz | 0.003 |
Dielectric strength K20/K20
(in transformer oil) Tested to IEC 60243-1 |
kV/mm | 20 |
Comparative tracking index (CTI) Tested to IEC 60112 | 600 |